欢迎来到江油市龙海特钢有限公司

403Cb不锈钢锻造调质

403Cb不锈钢锻造调质

403Cb不锈钢锻造调质

产品参数

  1. 冶炼方式: AOD+ESR
  2. 执行标准: ASTM 、ASME 、AMS 、
  3. 产品尺寸: Dia.190mm x 350 x 3000mm
  4. 交货状态: 锻造 、调质 、
  5. 表面状态: 铣削 、
  6. 库存状态: 订货

产品详情

403Cb化学成分

C Si Mn P S Cr Mo Ni Nb V Pb Sn Al
0.13 - 0.18 ≤ 0.50 0.40 - 0.60 ≤ 0.025 ≤ 0.010 11.00 - 13.00 ≤ 0.20 ≤ 0.60 0.15 - 0.25 ≤ 0.10 ≤ 0.005 ≤ 0.05 ≤ 0.05

403Cb力学性能

热处理 最小值 最大值 近似值 备注
热处理 最小值 最大值 近似值 备注
热处理 最小值 最大值 近似值 备注
热处理 最小值 最大值 近似值 备注
热处理 最小值 最大值 近似值 备注
热处理 类型 最小值 最大值 近似值 备注

403Cb Steel bars and forgings for blade manufacture

This specification covers one (1) grade of specialty martensitic stainless steel, commonly referred to the designation 403Cb. This material is used primarily for turbine and compressor components in applications requiring high strength and corrosion resistance to 900℉.
The bar materials supplied to this specification shall conform to ASTM A1028-03 Grade E class 2, and forgings shall confirm to ASTM A982-2 Grade E class 2. with supplementary requirements S1 and S7. and with exceptions as noted in this standard.

Process: AOD+ESR or other.

Chemical Composition

Carbon(C) 0.130.18
Manganese(Mn) 0.400.60
Phosphorus(P) 0.03max
Sulfur(S) 0.03max
Silicon(Si) 0.50max
Nickel(Ni) 0.75max
Chromium(Cr) 11.5-13
Molybdenum(Mo) 0.20max
Aluminum(Al) 0.05max
Vanadium(V) 0.10max
Niobium(Columbium) (Nb) 0.150.25

Heal Treatment

  • 4.1 Austenitizing Material shall be heated to 1725-1775 °F and held for a period of time long enough to ensure a uniform temperature of the core of each part in the load, but not less than two hours.
  • Quenching Oil quench to below 600 °F followed by air cooling to room temperature for complete transformation.
  • Tempering Material shall be tempered at a temperature not lower than 1150°F holding at temperature not less than (1) hour per inch of part thickness. Uniformly cool below the martensite finish temperature. Actual temper temperature will be adjusted to meet the mechanical properties shown in section (5).
  • Stress Relief Anneal A stress relief anneal is required after all final straightening, This includes any localized gag or press straightening. Material shall be stress relieved at 50 °F below the final tempering temperature.

Mechanical Properties

  • Tensile strength: min, 115,000 psi.
  • Yield strength: min. 100,000 psi (@ 0.2% offset)
  • Elongation in 2 in.: min. 20%
  • Reduction of area: min. 55%
  • Charpy impact energy avg. of three (3) specimens: 40(ft. tbs.) Charpy impact energy min. for any one (1) sample: 35 (ft. lbs.)
  • Brinell hardness of bars and forgings: 248 - 270 (BHN)

产品包装及运输