17-4PH

17-4PH

17.4PH, 0Cr17Ni4Cu4Nb, SAE AMS 5342E (2006) Steel, Corrosion-Resistant, Investment Castings 16Cr - 4 1Ni - 0 28Cb (Nb) - 3 2Cu Homogenization, Solution, and Precipitation Heat Treated (H1100) 130 ksi (896 MPa) Tensile Strength (17-4) Used typically for parts requiring good corr

17-4PH数据表下载

17-4PH化学成分 - SAE AMS 5342E (2006)

C Si Mn Cr Ni Cu Nb
≤0.07 ≤1.00 ≤1.00 15.00-17.50 3.00-5.00 3.00-5.00 0.15-1.45

17-4PH标准规范

  • SAE AMS 5342E (2006) - Steel, Corrosion-Resistant, Investment Castings 16Cr - 4.1Ni - 0.28Cb (Nb) - 3.2Cu Homogenization, Solution, and Precipitation Heat Treated (H1100) 130 ksi (896 MPa) Tensile Strength (17-4)
  • SAE AMS 5343E (2006) - Steel, Corrosion-Resistant, Investment Castings 16Cr - 4.1Ni - 0.28Cb (Nb) - 3.2Cu Homogenization, Solution, and Precipitation Heat Treated (H1000) 150 ksi (1034 MPa) Tensile Strength (17-4)
  • SAE AMS 5344F (2007) - Steel, Corrosion-Resistant, Investment Castings 16Cr - 4.1Ni - 0.28Cb - 3.2Cu Homogenization, Solution, and Precipitation Heat Treated (H900) 180 ksi (1241 MPa) Tensile Strength (17-4)
  • SAE AMS 5604G (2013) - Steel, Corrosion Resistant, Sheet, Strip, and Plate 16.5Cr - 4.0Ni - 4.0Cu - 0.30Cb Solution Heat Treated, Precipitation Hardenable
  • SAE AMS 5622F (2013) - Steel, Corrosion-Resistant, Bars, Wire, Forgings, Tubing, and Rings 16Cr - 4.0Ni - 0.30Cb - 4.0Cu Solution Heat Treated, Precipitation Hardenable Consumable Electrode Remelted
  • SAE AMS 5643/H1150 (2013) - Steel, Corrosion-Resistant, Bars, Wire, Forgings, Tubing and Rings 16Cr – 4.0Ni – 0.30Cb (Nb) – 4.0Cu Solution and Precipitation Heat Treated (H1150)
  • SAE AMS 5643S (2013) - Steel, Corrosion-Resistant, Bars, Wire, Forgings, Tubing, and Rings 16Cr - 4.0Ni - 0.30Cb - 4.0Cu Solution Heat Treated, Precipitation Hardenable

17-4PH机械性能

热处理 最小值 最大值 近似值 备注
热处理 最小值 最大值 近似值 备注
热处理 最小值 最大值 近似值 备注
热处理 最小值 最大值 近似值 备注
热处理 最小值 最大值 近似值 备注
热处理 Type 最小值 最大值 近似值 备注

SAE AMS 5342E (2006) Steel, Corrosion-Resistant, Investment Castings 16Cr - 4.1Ni - 0.28Cb (Nb) - 3.2Cu Homogenization, Solution, and Precipitation Heat Treated (H1100) 130 ksi (896 MPa) Tensile Strength (17-4) Used typically for parts requiring good corrosion resistance and strength up to 315°C.


17-4PH库存信息

钢号 规格mm 重量kg
05Cr17Ni4Cu4Nb, 0Cr17Ni4Cu4Nb φ50 x 4000mm 1
05Cr17Ni4Cu4Nb, 0Cr17Ni4Cu4Nb φ70 x 7000mm 0.73
05Cr17Ni4Cu4Nb, 0Cr17Ni4Cu4Nb φ80 x 7000mm 1.223
05Cr17Ni4Cu4Nb, 0Cr17Ni4Cu4Nb φ95 x 5500mm 0.7
05Cr17Ni4Cu4Nb, 0Cr17Ni4Cu4Nb φ100 x 6000mm 5
05Cr17Ni4Cu4Nb,0Cr17Ni4Cu4Nb φ95×16x4500mm 1400
05Cr17Ni4Cu4Nb,0Cr17Ni4Cu4Nb φ105×10x7000mm 3700

17-4PH产品形态